Alumina Green Body — Sintering

An alumina green body was tested with the DIL 402 C employing the NETZSCH Rate-Controlled Sintering (RCS)The properties of sintered products, such as density or particle size distribution, are determined by the sintering conditions (temperature, atmosphere, etc.) and especially by the sintering rates. Rate Controlled Sintering (Rate-Controlled Sintering (RCS)The properties of sintered products, such as density or particle size distribution, are determined by the sintering conditions (temperature, atmosphere, etc.) and especially by the sintering rates. RCS) software.

The measurement was carried out at a heating rate of 10 K/min. The start/stop mode of the Rate-Controlled Sintering (RCS)The properties of sintered products, such as density or particle size distribution, are determined by the sintering conditions (temperature, atmosphere, etc.) and especially by the sintering rates. RCS software was used. The threshold value was 10 µm/min (0.046 %/min). The heating rate was reduced by Rate-Controlled Sintering (RCS)The properties of sintered products, such as density or particle size distribution, are determined by the sintering conditions (temperature, atmosphere, etc.) and especially by the sintering rates. RCS during SinteringSintering is a production process for forming a mechanically strong body out of a ceramic or metallic powder. sintering to achieve a constant shrinkage rate. The influence of additives (e.g. organic binder, clays) was measured up to 1150°C. The main SinteringSintering is a production process for forming a mechanically strong body out of a ceramic or metallic powder. sintering step occured between 1150°C and 1350°C.