Introduction
Many complex fluids, such as network forming polymers, surfactant mesophases and concentrated emulsions do not flow until the applied StressStress is defined as a level of force applied on a sample with a well-defined cross section. (Stress = force/area). Samples having a circular or rectangular cross section can be compressed or stretched. Elastic materials like rubber can be stretched up to 5 to 10 times their original length.stress exceeds a certain critical value, known as the yield StressStress is defined as a level of force applied on a sample with a well-defined cross section. (Stress = force/area). Samples having a circular or rectangular cross section can be compressed or stretched. Elastic materials like rubber can be stretched up to 5 to 10 times their original length.stress. Materials exhibiting this behavior are said to be exhibiting yield flow behavior. The yield StressStress is defined as a level of force applied on a sample with a well-defined cross section. (Stress = force/area). Samples having a circular or rectangular cross section can be compressed or stretched. Elastic materials like rubber can be stretched up to 5 to 10 times their original length.stress is therefore defined as the StressStress is defined as a level of force applied on a sample with a well-defined cross section. (Stress = force/area). Samples having a circular or rectangular cross section can be compressed or stretched. Elastic materials like rubber can be stretched up to 5 to 10 times their original length.stress that must be applied to the sample before it starts to flow. Below the yield StressStress is defined as a level of force applied on a sample with a well-defined cross section. (Stress = force/area). Samples having a circular or rectangular cross section can be compressed or stretched. Elastic materials like rubber can be stretched up to 5 to 10 times their original length.stress, the sample will deform elastically (like stretching a spring), above the yield StressStress is defined as a level of force applied on a sample with a well-defined cross section. (Stress = force/area). Samples having a circular or rectangular cross section can be compressed or stretched. Elastic materials like rubber can be stretched up to 5 to 10 times their original length.stress the sample will flow like a liquid.
Most fluids with yield StressStress is defined as a level of force applied on a sample with a well-defined cross section. (Stress = force/area). Samples having a circular or rectangular cross section can be compressed or stretched. Elastic materials like rubber can be stretched up to 5 to 10 times their original length.stress can be considered as a structural skeleton that extends over the entire volume of the system. The strength of the skeleton is governed by the structure of the dispersed phase and its interactions. Normally, the continuous phase is low in viscosity, however, high volume fractions of a dispersed phase can increase the viscosity by a thousand times and induce solid-like behavior at rest.
When a complex fluid that exhibits yield behavior is sheared at low shear rates, in the range between 0.01 - 0.1 s-1 and below its critical StrainStrain describes a deformation of a material, which is loaded mechanically by an external force or stress. Rubber compounds show creep properties, if a static load is applied.strain, the system is subjected to work hardening. This is characteristic of solidlike behavior and results from elastic elements being stretched in the shear field. When such elastic elements approach their critical StrainStrain describes a deformation of a material, which is loaded mechanically by an external force or stress. Rubber compounds show creep properties, if a static load is applied.strain, the structure begins to break down causing Shear ThinningThe most common type of non-Newtonian behavior is shear thinning or pseudoplastic flow, where the fluid viscosity decreases with increasing shear.shear thinning (StrainStrain describes a deformation of a material, which is loaded mechanically by an external force or stress. Rubber compounds show creep properties, if a static load is applied.strain softening) and subsequent flow. This coincides with a peak value in shear StressStress is defined as a level of force applied on a sample with a well-defined cross section. (Stress = force/area). Samples having a circular or rectangular cross section can be compressed or stretched. Elastic materials like rubber can be stretched up to 5 to 10 times their original length.stress, which is equal to the yield StressStress is defined as a level of force applied on a sample with a well-defined cross section. (Stress = force/area). Samples having a circular or rectangular cross section can be compressed or stretched. Elastic materials like rubber can be stretched up to 5 to 10 times their original length.stress. This is depicted in Figure 1.
Yield StressStress is defined as a level of force applied on a sample with a well-defined cross section. (Stress = force/area). Samples having a circular or rectangular cross section can be compressed or stretched. Elastic materials like rubber can be stretched up to 5 to 10 times their original length.stress is defined as the stress that must be applied to the sample before it starts to flow.
Usually, a low shear rate is employed in these tests to account for time RelaxationWhen a constant strain is applied to a rubber compound, the force necessary to maintain that strain is not constant but decreases with time; this behavior is known as stress relaxation. The process responsible for stress relaxation can be physical or chemical, and under normal conditions, both will occur at the same time. relaxation properties of the material although different shear rates can be employed depending on the application of interest. Fast processes such as dispensing occur on short timescales which corresponds with higher shear rates while stability to sedimentation/ creaming occurs over longer times and is better evaluated at lower shear rates. Since Yield StressYield stress is defined as the stress below which no flow occurs; literally behaves like a weak solid at rest and a liquid when yielded.yield stress is generally a time dependent property then the measured values can be different. A shear rate of 0.01 s-1 is, however, commonly used in such a test and has been found to give good agreement with other Yield StressYield stress is defined as the stress below which no flow occurs; literally behaves like a weak solid at rest and a liquid when yielded.yield stress methods such as CreepCreep describes a time and temperature dependent plastic deformation under a constant force. When a constant force is applied to a rubber compound, the initial deformation obtained due to the application of the force is not fixed. The deformation will increase with time.creep testing [1].
This application note shows methodology and data from a stress growth test for a body lotion.
Experimental
- A commercial body lotion product was chosen for analysis.
- Rotational rheometer measurements were made using a Kinexus rheometer with a Peltier plate cartridge and 40 mm roughened parallel plates measuring system (to avoid sample slip at the geometry surfaces)2, and utilizing standard pre-configured sequences in rSpace software.
- The shear position for the parallel plate geometry was set to 100% in the rSpace software (using the geometry database) so as to measure the stress at the onset of yield.
- A standard loading sequence was used to ensure that the sample was subject to a consistent and controllablee loading protocol.
- A single shear rate test was performed at a shear rate of 0.01 s-1, and the stress evolution as a function of time was measured.
- The data was analyzed using a peak analysis to determine the Yield StressYield stress is defined as the stress below which no flow occurs; literally behaves like a weak solid at rest and a liquid when yielded.yield stress.
- All rheology measurements were performed at 25°C.
Results and Discussion
Figure 2 shows a stress versus time curve for the body lotion sample. The stress originally builds up as the StrainStrain describes a deformation of a material, which is loaded mechanically by an external force or stress. Rubber compounds show creep properties, if a static load is applied.strain is increased and reaches a peak value at the critical StrainStrain describes a deformation of a material, which is loaded mechanically by an external force or stress. Rubber compounds show creep properties, if a static load is applied.strain, which is equal to the Yield StressYield stress is defined as the stress below which no flow occurs; literally behaves like a weak solid at rest and a liquid when yielded.yield stress.
Table 1: Peak analysis results from stress evolution curve for body lotion sample
| Sample Description | Pure Body Lotion |
|---|---|
| Experiment name | Determining yield stress by stress growth |
| Action name | Yield stress analysis Point index |
| Point index | 1 |
| Shear stress (Pa) | 75.42 |
Shear viscosity (Pas) | 7.53E+003 |
This peak value is determined automatically from a peak analysis and reported back in the rSpace software in tabular form as shown in Table 1. The reported yield stress value for this body lotion is 75.4 Pa and this was found to occur at a StrainStrain describes a deformation of a material, which is loaded mechanically by an external force or stress. Rubber compounds show creep properties, if a static load is applied.strain of approximately 0.5 (50%).
As mentioned in the introduction, for some materials the measured yield stress can be shear rate dependent, especially when significant structural RelaxationWhen a constant strain is applied to a rubber compound, the force necessary to maintain that strain is not constant but decreases with time; this behavior is known as stress relaxation. The process responsible for stress relaxation can be physical or chemical, and under normal conditions, both will occur at the same time. relaxation occurs with time. In these instances, a higher yield stress will be observed for higher shear rates since there is less time for the structure to relax.
For example the same stress growth test performed on the same body lotion at a shear rate of 0.1 s-1 instead of 0.01 s-1 gave a yield stress of 82 Pa.
Conclusion
StressStress is defined as a level of force applied on a sample with a well-defined cross section. (Stress = force/area). Samples having a circular or rectangular cross section can be compressed or stretched. Elastic materials like rubber can be stretched up to 5 to 10 times their original length.Stress growth is a quick and accurate test for determining yield stress of a material. It is important, however, to employ a constant shear rate for comparative testing since different shear rates may give different results depending on the RelaxationWhen a constant strain is applied to a rubber compound, the force necessary to maintain that strain is not constant but decreases with time; this behavior is known as stress relaxation. The process responsible for stress relaxation can be physical or chemical, and under normal conditions, both will occur at the same time. relaxation behavior of the material being tested.
Please note ...
that testing can be undertaken with cone and plate or parallel plate geometry – with the latter being preferred for dispersions and emulsions with large particle sizes. Such material types may also require the use of serrated or roughened geometries to avoid artefacts relating to slippage at the geometry surface.