Cuerpo Sin Procesar de Alumina — Sinterización

Un cuerpo sin procesar (crudo) de alumina se probó con el DIL 402 C empleando el software de Sinterización Controlada por Tasa (Rate-Controlled Sintering (RCS)The properties of sintered products, such as density or particle size distribution, are determined by the sintering conditions (temperature, atmosphere, etc.) and especially by the sintering rates. RCS) de NETZSCH.

La medición se realizó empleando una tasa de calentamiento de 10 K/min. Se utilizó el modo inicio/detención del software Rate-Controlled Sintering (RCS)The properties of sintered products, such as density or particle size distribution, are determined by the sintering conditions (temperature, atmosphere, etc.) and especially by the sintering rates. RCS. El valor del umbral era 10 µm/min (0,046 %/min). La tasa de calentamiento se redujo mediante el Rate-Controlled Sintering (RCS)The properties of sintered products, such as density or particle size distribution, are determined by the sintering conditions (temperature, atmosphere, etc.) and especially by the sintering rates. RCS durante la sinterización para lograr una tasa de contracción constante. La influencia de los aditivos (ejemplo; aglutinador orgánico, arcillas) se midió bajo temperaturas de hasta 1150°C. El paso de sinterización principal se produjo entre 1150°C y 1350°C.