PbTe – A Thermoelectric Material Heat Capacity and Thermal Conductivity

Introduction

Thermoelectric substances are promising materials for waste heat harvesting. Examples of this would be the generation of electric energy by converting the heat of automobile exhaust, or from cooling devices used in power plants. Important physical properties to consider are the so-called Seebeck coefficient (S) and Thermal ConductivityThermal conductivity (λ with the unit W/(m•K)) describes the transport of energy – in the form of heat – through a body of mass as the result of a temperature gradient (see fig. 1). According to the second law of thermodynamics, heat always flows in the direction of the lower temperature.thermal conductivity δ). The well-known figure of merit (Z) describes the efficiency of such materials:

ZT = (S2 λ-1

with

From the formula, it can be concluded that for a high Z value, the material should have a high Seebeck effect and a low Thermal ConductivityThermal conductivity (λ with the unit W/(m•K)) describes the transport of energy – in the form of heat – through a body of mass as the result of a temperature gradient (see fig. 1). According to the second law of thermodynamics, heat always flows in the direction of the lower temperature.thermal conductivity value.

PbTe is a potential candidate for such applications as it has a moderate Seebeck coefficient and a relatively low Thermal ConductivityThermal conductivity (λ with the unit W/(m•K)) describes the transport of energy – in the form of heat – through a body of mass as the result of a temperature gradient (see fig. 1). According to the second law of thermodynamics, heat always flows in the direction of the lower temperature.thermal conductivity

Results and Discussion

The specific heat of PbTe samples were measured with the NETZSCH DSC 204 F1 Phoenix® in the temperature range from RT to 300°C using the ratio method.

Figure 1 depicts the cp curve of the PbTe sample. The specific heat values are in the range of 0.15 J/(g*K) to 0.16 J/(g*K) which is typical for this material.

λ(T) = a(T) ∙ cp(T) ∙ ρ(T)

with

Summary

The Thermal DiffusivityThermal diffusivity (a with the unit mm2/s) is a material-specific property for characterizing unsteady heat conduction. This value describes how quickly a material reacts to a change in temperature.thermal diffusivity and specific heat of PbTe were measured with LFA and DSC instrumentation, respectively. The Thermal ConductivityThermal conductivity (λ with the unit W/(m•K)) describes the transport of energy – in the form of heat – through a body of mass as the result of a temperature gradient (see fig. 1). According to the second law of thermodynamics, heat always flows in the direction of the lower temperature.thermal conductivity, which is a very important physical property for the evaluation of efficiency of thermoelectric materials, was calculated utilizing this data along with the DensityThe mass density is defined as the ratio between mass and volume. density of the material. The PbTe showed the expected decrease in thermal con-ductivity with increasing temperature as is normally observed for other semiconducting materials.