Analysis of Ethylene Vinyl Acetate (EVA) (TGA-FT-IR)

The 3-D plot shows a TGA-FT-IR measurement on an EVA sample between 25°C and 600°C.

The mass-loss steps of the EVA sample (TGA, black curve) correlate well with the absorption intensities between 650 cm-1 and 4000 cm-1. The evolved gases as 2-dimensional spectra can be extracted at any desired temperature and subjected to a library search (e.g., NIST-EPA library for evolved gases) for identification.

The lower plot shows the TGA (black), DTGA (black dashed) and the Gram-Schmidt graph (blue). The two additional extracted traces (temperature-dependent intensities; red and green curves) are in very good correlation with the DTGA curve. The 1st mass-loss step at 350°C is due to the release of acetic acid (red curve). In the 2nd mass-loss step, acetic acid has already been totally released. The green curve represents the absorption intensities of the released hydrocarbons resulting from the Reazione di DecomposizioneA decomposition reaction is a thermally induced reaction of a chemical compound forming solid and/or gaseous products. decomposition of the polymer backbone (DTGA peak at 468°C).

*Gram-Schmidt: Total intensity of the obtained infrared spectra of the gases released

3-D plot of the temperature-dependent FT-IR measurement with integrated TGA (black) curve of an EVA sample (upper plot). The TGA (black solid) and DTGA (black dashed) curves are in correlation with the Gram-Schmidt (blue) and single absorption intensities of acetic acid (red) and CH (green), respectively (lower plot). Measurement conditions: sample mass: 8.75 mg; crucible: Al2O3; atmosphere: N2 (40 ml/min); heating rate: 10 K/min.