A major source of failure of electronic assemblies is thermal expansion and the problems it causes. Thermomechanical Analysis can help in avoiding those product failures.
FR4 – most commonly used composite in the electronic industry
FR4 (FR= flame retardant) and its derivates (FR2, FR3, FR5) are by far the most widely used base materials for electronic circuit boards and electronic assemblies. The FR4’s backing material exists of fiberglass woven into a thin, cloth-like sheet. The glass fabric is then impregnated with a flame-retardant epoxy resin. The resulting low cost composite is stiff, insulates reliably and performs well in most environmental conditions. On the flip side, the epoxy resin matrix has a lower Tg and higher thermal expansion coefficient than the reinforcing glass fabric and tends to soften and expand when a circuit board goes through several thermal cycles in the production process and potentially during use. This can lead to a partial detachment of the pressed material compound, which, in turn, leads to joint failures or DelaminationUnter Delamination versteht man eine Trennung von z.B. Harz vom Laminat oder Fasern vom Harz, was Defekte in Leiterplatten verursacht.delamination. The consequence is usually a failure of the assembly. Thermomechanical analysis (TMA) is a good method to measure thermal expansion of the circuit board base, electronic components, and component materials.
To make sure that the circuit base boards conform to a certain quality, IPC standards were put into place that require measurement of the thermal expansion, glass transition and softening point [see IPC-TM-650 220.127.116.11 Time to DelaminationUnter Delamination versteht man eine Trennung von z.B. Harz vom Laminat oder Fasern vom Harz, was Defekte in Leiterplatten verursacht.Delamination (TMA Method)].
CTE and Tg – Two important values for the quality control of FR4 composites
The important material characteristic for quality assurance of polymer composites like FR4 is the glass transition temperature, Tg. This is the temperature point where the epoxy resin structure starts to soften. As soon as the Tg value is reached, the material starts to expand more – typically between 2-3 times more than in the solid state. Thermomechanical analysis (TMA) is a perfect tool for studying the expansion behavior and softening temperature of various materials such as polymers, elastomers and composites. It provides fundamental information about the coefficient of thermal expansion (CTE), the glass transition temperature as well as about viscoelastic properties. It is a very sensitive method and can be used to determine weak physical transitions that are associated with changes in modulus, curing, or delamination, which sometimes cannot be detected by Differential Scanning Calorimetry (DSC).
This makes it the method of choice for quality control. Testing the maximum processing temperature of your FR4 reduces the probability of the Printed Circuit Board (PCB) being damaged during component production.
Time to Delamination – visible product failure
The PCB gets subjected to thermal stress during assembly, for example, in the reflow soldering oven. The time to delamination is important when it comes to the material selection for a certain application. The figure below shows a measurement on an FR4 sample in which the time to delamination was recorded. Two measurements were conducted. In both, the sample was heated to the testing temperature. Then one was kept at an isothermal temperature of 260°C (according to IPC standard) and a second one with an isothermal temperature of 300°C. In the first measurement at 260°C (green line), the TMA did not detect delamination as the curve stays flat until the end of the measurement. However, at the higher temperature of 300°C, degradation of the product is visible. The second measurement, records a Time to Delamination at 18.1 min after being held at an isothermal temperature of 300°C, which was reached 28 min after the start of the measurement. The TMA clearly detects the delamination, where the physical inspection of the sample only shows some discoloration as can be seen in photos taken of the different samples before and after the tests.
This test has become especially important ever since the “Restriction of Hazardous Substances Directive” 2002/95/EC (RoHS 1) took effect in the European Union. In the case of electronic and electrical equipment, this affects, for example, the use of lead-containing solders. Equipment produced or sold to the EU market now has to be lead-free. This had a major effect on the required thermal stability of all components – including FR4.
The processes to produce lead-free solders now require reflow temperatures of up to 260°C. Prior reflow temperatures were only at 240°C. The FR4 used for this study would be suitable for both the leaded and the lead-free solders, as the delamination effects were not detected until a temperature of 300°C was reached. However, not all materials that are currently used as base materials for electronic circuit boards and electronic assemblies may withstand the new requirements of lead-free processes.
The above investigation with TMA shows how important the determination of Time to Delamination is to avoid product failure and supply your customers with high-quality products. Thermomechanical Analysis is applied according to IPC standard to test for material suitability. The new TMA 402 F3 Hyperion® Polymer Edition is specifically designed to measure a wide range of polymer materials and is well suited for the quality control needs of the electronic component industry.